グリーンエメリーSIC 99%
グリーンエメリー SIC 99% 一般的な化学分析 [%]
| SiC | Fe2O3 _ _ _ | FC | F.Si | SiO2_ _ | 法 |
| ≧99.0 | ≤0.40 | ≤0.20 | ≤0.20 | ≤0.50 | < 0.05 |
グリーン炭化ケイ素 PSD 粒子サイズ分布
| F008 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≧70% | -1700um | ≤3% |
| F010 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≧70% | -1400um | ≤3% |
| F012 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≧70% | -1180um | ≤3% |
| F014 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≧70% | -1000um | ≤3% |
| F016 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≧70% | -850um | ≤3% |
| F020 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≧70% | -710um | ≤3% |
| F022 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≧70% | -600um | ≤3% |
| F024 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500um | ≤3% |
| F030 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
| F036 | +850um | 0 | +600um | ≤25% | +500um | ≥45% | +500+425um | ≥65% | -355um | ≤3% |
| F046 | +600um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250um | ≤3% |
| F054 | +500um | 0 | +355um | ≤30% | +300um | ≥40% | +300+250um | ≥65% | -212um | ≤3% |
| F060 | +425um | 0 | +300um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
| F070 | +355um | 0 | +250um | ≤25% | +212um | ≥40% | +212+180um | ≥65% | -150um | ≤3% |
| F080 | +300um | 0 | +212um | ≤25% | +180um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
| F090 | +250um | 0 | +180um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
| F100 | +212um | 0 | +150um | ≤20% | +125um | ≥40% | +125+106um | ≥65% | -75um | ≤3% |
| F120 | +180um | 0 | +125um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63um | ≤3% |
| F150 | +150um | 0 | +106um | ≤15% | +75um | ≥40% | +75+63um | ≥65% | -45um | ≤3% |
| F180 | +125um | 0 | +90um | ≤15% | +75um | * | +75+63um | ≥40% | -53um | * |
| F220 | +106um | 0 | +75um | ≤15% | +63um | * | +63+53um | ≥40% | -45um | * |
グリーンエメリー SIC 99% 主な用途:
-結合研磨材およびコーティング研磨材
-ブラスト、表面処理、錆取り
-湿式および乾式ブラストメディア、研削および研磨など
-床/壁ラミネート、耐摩耗性
-セラミック製品: セラミックとタイル、セラミックフィルタープレート、セラミック膜など
・テフロン塗装等
– 断熱材
-砥石、カップホイール、砥石、研磨パッドなど
-るつぼ、窯焼成部品、メカニカルシール、半導体製造用部品材料などに使用されます。
パッキング：
 |
 |
 |
 |
| 25kgのPVCバッグ | 1メートルの大きなバッグ | 25kgs PVCバッグ+1mtビッグバッグ | 25kgs PVCバッグ+パレット |