緑色炭化ケイ素の典型的な化学分析 [%]
| SiC |
Fe2O3 |
FC |
F.Si |
SiO2 |
法 |
| 98.0～99.5 |
≤0.15 |
≤0.30 |
≤0.40 |
≤0.70 |
<0.09 |
グリーン炭化ケイ素の物理的特性
| 比重 |
3.95g/cm3 |
| モース硬度 |
9.4 |
| 最高使用温度 |
1900℃ |
| 融点 |
2250℃ |
グリーン炭化ケイ素の粒径分布
| F16 |
+2000um |
0 |
+1400um |
≤20% |
+1180um |
≥45% |
+1180+1000um |
≧70% |
-850um |
≤3% |
| F20 |
+1700um |
0 |
+1180um |
≤20% |
+1000um |
≥45% |
+1000+850um |
≧70% |
-710um |
≤3% |
| F22 |
+1400um |
0 |
+1000um |
≤20% |
+850um |
≥45% |
+850+710um |
≧70% |
-600um |
≤3% |
| F24 |
+1180um |
0 |
+850um |
≤25% |
+710um |
≥45% |
+710+600um |
≥65% |
-500um |
≤3% |
| F30 |
+1000um |
0 |
+710um |
≤25% |
+600um |
≥45% |
+600+500um |
≥65% |
-425um |
≤3% |
| F36 |
+850um |
0 |
+600um |
≤25% |
+500um |
≥45% |
+500+425um |
≥65% |
-355um |
≤3% |
| F46 |
+600um |
0 |
+425um |
≤30% |
+355um |
≥40% |
355+300um |
≥65% |
-250um |
≤3% |
| F54 |
+500um |
0 |
+355um |
≤30% |
+300um |
≥40% |
+300+250um |
≥65% |
-212um |
≤3% |
| F60 |
+425um |
0 |
+300um |
≤30% |
+250um |
≥40% |
250+212um |
≥65% |
-180um |
≤3% |
| F70 |
+355um |
0 |
+250um |
≤25% |
+212um |
≥40% |
+212+180um |
≥65% |
-150um |
≤3% |
| F80 |
+300um |
0 |
+212um |
≤25% |
+180um |
≥40% |
+180+150um |
≥65% |
-125um |
≤3% |
| F90 |
+250um |
0 |
+180um |
≤20% |
+150um |
≥40% |
+150+125um |
≥65% |
-106um |
≤3% |
| F100 |
+212um |
0 |
+150um |
≤20% |
+125um |
≥40% |
+125+106um |
≥65% |
-75um |
≤3% |
| F120 |
+180um |
0 |
+125um |
≤20% |
≥40% |
≥40% |
+106+90um |
≥65% |
-63um |
≤3% |
| F150 |
+150um |
0 |
+106um |
≤15% |
+75um |
≥40% |
+75+63um |
≥65% |
-45um |
≤3% |
| F180 |
+125um |
0 |
+90um |
≤15% |
+75um |
* |
+75+63um |
≥40% |
-53um |
* |
| F220 |
+106um |
0 |
+75um |
≤15% |
+63um |
* |
+63+53um |
≥40% |
-45um |
* |
緑色炭化ケイ素第一章（JIS規格）
| サイズ |
それをする） |
D3(うーん) |
D50(1本) |
D94(程度) |
| #240 |
≤127 |
≤103 |
57.0±3.0 |
40以上 |
| #280 |
≤112 |
≤87 |
48.0±3.0 |
≥33 |
| #320 |
≤98 |
≤74 |
40.0±2.5 |
≥27 |
| #360 |
≤86 |
≤66 |
35.0±2.0 |
≥23 |
| #400 |
≤75 |
≤58 |
30.0±2.0 |
20以上 |
| #500 |
≤63 |
≤50 |
25.0±2.0 |
≥16 |
| #600 |
≤53 |
≤41 |
20.0±1.5 |
≥13 |
| #700 |
≤45 |
≤37 |
17.0±1.5 |
≥11 |
| #800 |
≤38 |
≤31 |
14.0±1.0 |
≥9.0 |
| #1000 |
≤32 |
≤27 |
11.5±1.0 |
≧7.0 |
| #1200 |
≤27 |
≤23 |
9.5±0.8 |
≧5.5 |
| #1500 |
≤23 |
≤20 |
8.0±0.6 |
≥4.5 |
| #2000 |
≤19 |
≤17 |
6.7±0.6 |
≥4.0 |
| #2500 |
≤16 |
≤14 |
5.5±0.5 |
≧3.0 |
| #3000 |
≤13 |
≤11 |
4.0±0.5 |
≧2.0 |
| #4000 |
≤11 |
≤8.0 |
3.0±0.4 |
≥1.8 |
| #6000 |
≤8.0 |
≤5.0 |
2.0±0.4 |
≧0.8 |
| #8000 |
≤6.0 |
≤3.5 |
1.2±0.3 |
≧0.6 |
グリーンシリコンカーバイドチャプターⅡ（FEPA規格）
| サイズ |
D3(うーん) |
D50(1本) |
D94（μm） |
| F230 |
<82 |
53.0±3.0 |
>34 |
| F240 |
<70 |
44.5±2.0 |
>28 |
| F280 |
<59 |
36.5±1.5 |
>22 |
| F320 |
<49 |
29.2±1.5 |
>16.5 |
| F360 |
<40 |
22.8±1.5 |
>12 |
| F400 |
<32 |
17.3±1.0 |
>8 |
| F500 |
<25 |
12.8±1.0 |
>5 |
| F600 |
19 歳未満 |
9.3±1.0 |
>3 |
| F800 |
<14 |
6.5±1.0 |
>2 |
| F1000 |
<10 |
4.5±0.8 |
>1 |
| F1200 |
<7 |
3.0±0.5 |
>1(80%) |
| F1500 |
<5 |
2.0±0.4 |
>0.8(80%) |
| F2000 |
<3.5 |
1.2±0.3 |
>0.5(80%) |
グリーンシリコンカーバイドの主な用途
- 結合研磨材とコーティング研磨材
- ブラスト処理、表面処理、錆取り
- 湿式・乾式ブラストメディア、研削・研磨など
- 床/壁ラミネート、耐摩耗性
- セラミック製品：セラミックとタイル、セラミックフィルタープレート、セラミック膜など
- テフロン塗装など
- 断熱材
- 砥石、カップホイール、砥石、研磨パッドなど
- るつぼ、焼成部品、メカニカルシール、半導体製造用部品材料などに使用されます。
梱包
25kgs PVC バッグ + 1mt ビッグバッグ
25kgs PVC バッグ + パレット